Vickers hardness measurements confirm that all samples demonstrated the reverse indentation size effect, indicating an increment in hardness values with an applied load across all samples. 维氏硬度测试证实，全部样品均表现出反向压痕尺寸效应，意味着所有样品的硬度值都会随外加载荷增大而升高。
Further, the microindentation hardness measurements underwent semi-empirical analysis through several models. 此外，本文采用多种模型对显微压痕硬度测试结果开展半经验分析。
After comparison, the Indentation-Induced Cracking model is identified as the best fit, providing parameters that aligned most closely with the load-independent microhardness results. 经过对比，压痕致开裂模型被确定为最优拟合模型，由该模型得到的参数和与载荷无关的显微硬度结果吻合度最高。
反向压痕尺寸效应（RISE）